- 密度 [g/cm3]: 1.54
- 缺口冲击强度: 0.59
- 断裂伸长率 [%]: 130
- 弯曲强度 [MPa]: 95.0
- 弯曲模量 [MPa]: 8.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.54 g/cc | 0.0556 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage | 0.0075 - 0.0095 cm/cm | 0.0075 - 0.0095 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.0090 cm/cm | 0.0070 - 0.0090 in/in | DIS 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 95.0 MPa | 13800 psi | ISO 527-93 |
| Elongation at Break | 2.0 % | 2.0 % | ISO 527-93 |
| Flexural Yield Strength | 130 MPa | 18900 psi | ISO 178-93 |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ISO 178-93 |
| Izod Impact, Notched | 0.590 J/cm | 1.11 ft-lb/in | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 250 °C | 482 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75-93 |