- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 1.33
- 缺口冲击强度: 3.0
- 弯曲模量 [MPa]: 2.70
- 透光率 [%]: 87.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in³ | ISO 1183-87 |
| Linear Mold Shrinkage | 0.0010 - 0.0050 cm/cm | 0.0010 - 0.0050 in/in | ISO DIS 294-4 |
| Melt Flow | 3.5 g/10 min @Load 0.325 kg, Temperature 280 °C | 3.5 g/10 min @Load 0.716 lb, Temperature 536 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 79 | 79 | ASTM D-2240 |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-93 |
| Elongation at Break | 250 % | 250 % | ISO 527-93 |
| Flexural Strength | 60.0 MPa | 8700 psi | ISO 178-93 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178-93 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | ISO 180-93 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 245 °C | 473 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-93 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D-2240 |
| Transmission, Visible | 87 % | 87 % | ASTM D-1003 |