- 缺口冲击强度: 0.32
- 弯曲模量 [MPa]: 4.00
- 硬度: 122.0
- 热变形温度 [℃]: 259.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm @Thickness 3.20 mm | 0.0060 in/in @Thickness 0.126 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 122 | 122 | ASTM D785 |
| Tensile Strength at Break | 62.0 MPa | 8990 psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 4.00 GPa | 580 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm | 0.600 ft-lb/in | ASTM D256 |
| 0.320 J/cm @Temperature -40.0 °C | 0.600 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |
| Izod Impact, Unnotched | 2.56 J/cm | 4.80 ft-lb/in | ASTM D4812 |
| 2.14 J/cm @Temperature -40.0 °C | 4.00 ft-lb/in @Temperature -40.0 °F | ASTM D4812 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 259 °C | 498 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 202 °C | 396 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 295 - 310 °C | 563 - 590 °F | 300°C Optimum |
| Mold Temperature | 150 - 175 °C | 302 - 347 °F | |
| Drying Temperature | 120 - 150 °C | 248 - 302 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | Dehumidified Dryer |
| Moisture Content | <= 0.030 % | <= 0.030 % | Processing Moisture Content |