- 密度 [g/cm3]: 1.51
- 缺口冲击强度: 1.471
- 断裂伸长率 [%]: 78.5
- 弯曲强度 [MPa]: 65.0
- 弯曲模量 [MPa]: 1.29
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.51 - 1.70 g/cc | 0.0546 - 0.0614 lb/in³ | Average value: 1.60 g/cc Grade Count:6 |
Linear Mold Shrinkage | 0.00200 - 0.00300 cm/cm | 0.00200 - 0.00300 in/in | Average value: 0.00275 cm/cm Grade Count:4 |
Linear Mold Shrinkage, Transverse | 0.00800 - 0.00900 cm/cm | 0.00800 - 0.00900 in/in | Average value: 0.00875 cm/cm Grade Count:4 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength, Ultimate | 65.0 - 130 MPa | 9430 - 18900 psi | Average value: 97.6 MPa Grade Count:5 |
Elongation at Break | 1.30 - 2.30 % | 1.30 - 2.30 % | Average value: 1.78 % Grade Count:6 |
Modulus of Elasticity | 5.10 - 13.0 GPa | 740 - 1890 ksi | Average value: 8.87 GPa Grade Count:5 |
Flexural Yield Strength | 78.5 - 178 MPa | 11400 - 25800 psi | Average value: 139 MPa Grade Count:3 |
Flexural Modulus | 1.29 - 8.00 GPa | 186 - 1160 ksi | Average value: 5.61 GPa Grade Count:3 |
Izod Impact, Notched | 1.471 - 1.56906 J/cm @Temperature -30.0 - -30.0 °C | 2.756 - 2.93950 ft-lb/in @Temperature -22.0 - -22.0 °F | Average value: 1.52 J/cm Grade Count:1 |
1.471 - 1.56906 J/cm @Thickness 3.17 - 6.35 mm | 2.756 - 2.93950 ft-lb/in @Thickness 0.125 - 0.250 in | Average value: 1.52 J/cm Grade Count:1 | |
Charpy Impact Unnotched | 2.60 - 5.50 J/cm² | 12.4 - 26.2 ft-lb/in² | Average value: 3.70 J/cm² Grade Count:4 |
Charpy Impact, Notched | 0.320 - 0.800 J/cm² | 1.52 - 3.81 ft-lb/in² | Average value: 0.543 J/cm² Grade Count:4 |
Thermal Properties | Metric | English | Comments |
CTE, linear | 24.0 - 32.0 µm/m-°C | 13.3 - 17.8 µin/in-°F | Average value: 28.7 µm/m-°C Grade Count:3 |
CTE, linear, Transverse to Flow | 75.0 - 102 µm/m-°C | 41.7 - 56.7 µin/in-°F | Average value: 92.3 µm/m-°C Grade Count:3 |
Melting Point | 285 °C | 545 °F | Average value: 285 °C Grade Count:4 |
Deflection Temperature at 1.8 MPa (264 psi) | 240 - 262 °C | 464 - 504 °F | Average value: 251 °C Grade Count:3 |
Processing Properties | Metric | English | Comments |
Processing Temperature | 80.0 - 150 °C | 176 - 302 °F | Average value: 120 °C Grade Count:4 |
Melt Temperature | 285 - 310 °C | 545 - 590 °F | Average value: 297 °C Grade Count:4 |
Drying Temperature | 95.0 - 100 °C | 203 - 212 °F | Average value: 96.3 °C Grade Count:4 |
Dry Time | 4.00 - 6.00 hour | 4.00 - 6.00 hour | Average value: 5.00 hour Grade Count:4 |
Moisture Content | 0.0300 % | 0.0300 % | Average value: 0.0300 % Grade Count:3 |