- 密度 [g/cm3]: 1.23
- 拉伸强度 [MPa]: 45.0
- 热变形温度 [℃]: 73.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 45.0 MPa | 6530 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | |
| Elongation at Yield | 4.2 % | 4.2 % | |
| Tensile Modulus | 2.13 GPa | 309 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.57 J/cm² | 7.47 ft-lb/in² | |
| 0.480 J/cm² @Temperature -30.0 °C | 2.28 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 78.0 µm/m-°C @Temperature 20.0 °C | 43.3 µin/in-°F @Temperature 68.0 °F | in flow direction |
| CTE, linear, Transverse to Flow | 60.0 µm/m-°C @Temperature 20.0 °C | 33.3 µin/in-°F @Temperature 68.0 °F | |
| Specific Heat Capacity | 1.34 J/g-°C | 0.320 BTU/lb-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 73.0 °C | 163 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.0 °C | 151 °F | |
| Vicat Softening Point | 80.0 °C | 176 °F | |
| Glass Transition Temp, Tg | 83.0 °C | 181 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 275 - 295 °C | 527 - 563 °F | |