- 熔体流动速率 [g/10min]: 20.0
- 密度 [g/cm3]: 0.925
- 拉伸强度 [MPa]: 12.1
- 脆化温度 [℃]: -100.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D1505 | ||
| Environmental Stress Crack Resistance | 25 hour | 25 hour | F50, 100% Igepal, Bent strip test, slit; ASTM D-1693 | ||
| Melt Flow | 20 g/10 min @Load 2.16 kg, Temperature 190 °C | 20 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 12.1 MPa | 1750 psi | 2 in/min (50 mm/min); ASTM D638 | ||
| Elongation at Break | 280 % | 280 % | 2 in/min (50 mm/min); ASTM D638 | ||
| Modulus of Elasticity | 0.324 GPa | 47.0 ksi | ASTM D-638 | ||
| Thermal Properties | Metric | English | Comments | ||
| Brittleness Temperature | <= -100 °C | <= -148 °F | ASTM D-746 | ||
| Descriptive Properties | |||||
| process | Injection Molding | ||||
| region | Europe/Turkey | ||||