- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.912
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.912 - 1.86 g/cc | 0.0329 - 0.0672 lb/in³ | Average value: 0.993 g/cc Grade Count:32 |
| Particle Size | 1.50 - 2.50 µm | 1.50 - 2.50 µm | Average value: 1.83 µm Grade Count:3 |
| Thickness | 20.3 - 31.8 microns | 0.800 - 1.25 mil | Average value: 24.8 microns Grade Count:23 |
| Melt Flow | 0.500 - 55.0 g/10 min | 0.500 - 55.0 g/10 min | Average value: 3.58 g/10 min Grade Count:32 |
| Antiblock Level | 2500 - 5000 ppm | 2500 - 5000 ppm | Average value: 4000 ppm Grade Count:6 |
| Slip Level | 450 - 1000 ppm | 450 - 1000 ppm | Average value: 750 ppm Grade Count:5 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.27 - 13.0 MPa | 1200 - 1890 psi | Average value: 9.88 MPa Grade Count:24 |
| Film Tensile Strength at Yield, TD | 7.00 - 15.0 MPa | 1020 - 2180 psi | Average value: 9.73 MPa Grade Count:24 |
| Film Elongation at Break, MD | 470 - 680 % | 470 - 680 % | Average value: 551 % Grade Count:28 |
| Film Elongation at Break, TD | 520 - 840 % | 520 - 840 % | Average value: 694 % Grade Count:28 |
| Secant Modulus | 0.170 - 0.240 GPa | 24.7 - 34.8 ksi | Average value: 0.204 GPa Grade Count:3 |
| Secant Modulus, MD | 0.101 - 0.241 GPa | 14.7 - 34.9 ksi | Average value: 0.166 GPa Grade Count:23 |
| Secant Modulus, TD | 0.124 - 0.333 GPa | 18.0 - 48.3 ksi | Average value: 0.183 GPa Grade Count:23 |
| Puncture Energy | 1.59 - 4.41 J | 1.17 - 3.25 ft-lb | Average value: 3.22 J Grade Count:15 |
| Coefficient of Friction | 0.220 - 0.800 | 0.220 - 0.800 | Average value: 0.530 Grade Count:3 |
| Elmendorf Tear Strength MD | 80.0 - 550 g | 80.0 - 550 g | Average value: 235 g Grade Count:11 |
| Elmendorf Tear Strength TD | 400 - 890 g | 400 - 890 g | Average value: 535 g Grade Count:11 |
| Elmendorf Tear Strength, MD | 6.30 - 27.0 g/micron | 160 - 686 g/mil | Average value: 11.1 g/micron Grade Count:18 |
| Elmendorf Tear Strength, TD | 16.0 - 31.0 g/micron | 406 - 787 g/mil | Average value: 20.1 g/micron Grade Count:18 |
| Dart Drop | 5.51 - 55.0 g/micron | 140 - 1400 g/mil | Average value: 18.3 g/micron Grade Count:18 |
| Dart drop Test | 70.0 - 290 g | 0.154 - 0.639 lb | Average value: 138 g Grade Count:14 |
| Film Tensile Strength at Break, MD | 30.0 - 75.8 MPa | 4350 - 11000 psi | Average value: 52.1 MPa Grade Count:28 |
| Film Tensile Strength at Break, TD | 20.0 - 65.5 MPa | 2900 - 9500 psi | Average value: 39.8 MPa Grade Count:28 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 114 - 127 °C | 237 - 260 °F | Average value: 119 °C Grade Count:22 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.40 - 42.0 % | 1.40 - 42.0 % | Average value: 14.9 % Grade Count:26 |
| Gloss | 11.0 - 95.0 % | 11.0 - 95.0 % | Average value: 44.6 % Grade Count:22 |
| Processing Properties | Metric | English | Comments |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:3 |