- 熔体流动速率 [g/10min]: 1.25
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 11.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 1.25 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.25 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 11.0 MPa | 1600 psi | TD; ISO 527-3 |
| Film Elongation at Break, MD | 550 % | 550 % | ISO 527-3 |
| Film Elongation at Break, TD | 710 % | 710 % | ISO 527-3 |
| Elmendorf Tear Strength, MD | 2.04 g/micron | 51.8 g/mil | ISO 6383/2 |
| Elmendorf Tear Strength, TD | 15.49 g/micron | 393.4 g/mil | ISO 6383/2 |
| Dart drop Test | 70.0 g @Thickness 0.0250 mm | 0.154 lb @Thickness 0.000984 in | ISO 7765-1 |
| Film Tensile Strength at Break, MD | 32.0 MPa | 4640 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | ISO 11357-3 |