- 熔体流动速率 [g/10min]: 0.55
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 38.0 microns | 1.50 mil | |||
| Melt Flow | 0.55 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.55 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 885 % | 885 % | ASTM D882 | ||
| Film Elongation at Break, TD | 1088 % | 1088 % | ASTM D882 | ||
| Secant Modulus, MD | 0.266 GPa | 38.6 ksi | 1%; ASTM D882 | ||
| Secant Modulus, TD | 0.320 GPa | 46.4 ksi | 1%; ASTM D882 | ||
| Coefficient of Friction | 0.67 | 0.67 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 10.6 g/micron | 269 g/mil | ASTM 1922 | ||
| Elmendorf Tear Strength, TD | 25.4 g/micron | 645 g/mil | ASTM 1922 | ||
| Dart Drop | 3.60 g/micron | 91.4 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 57.0 MPa | 8270 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 13.4 % | 13.4 % | ASTM D1003 | ||
| Gloss | 8.4 % | 8.4 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Additives | Antiblock and PPA | ||||
| Minimum Recommended Thickness | 45 µm | ||||