- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM-D792 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 788 % | 788 % | ASTM-D882 |
| Film Elongation at Break, TD | 937 % | 937 % | ASTM-D882 |
| Elmendorf Tear Strength MD | 108 g | 108 g | ASTM-D1922 |
| Elmendorf Tear Strength TD | 328 g | 328 g | ASTM-D1922 |
| Elmendorf Tear Strength, MD | 4.32 g/micron | 110 g/mil | ASTM-D1922 |
| Elmendorf Tear Strength, TD | 13.12 g/micron | 333.2 g/mil | ASTM-D1922 |
| Dart Drop | 4.08 g/micron | 104 g/mil | ASTM-D1709 |
| Dart drop Test | 102 g | 0.225 lb | ASTM-D1709 |
| Film Tensile Strength at Break, MD | 26.0 MPa | 3770 psi | ASTM-D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM-D882 |
| 1% Secant Modulus, MD | 201 MPa | 29200 psi | ASTM-D882 |
| 1% Secant Modulus, TD | 230 MPa | 33400 psi | ASTM-D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM-D1003 |
| Gloss | 114 % | 114 % | Angle 60°; ASTM-D2457 |