- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | ASTM D-1505 | ||
| Melt Index of Compound | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 400 % | 400 % | Blown Film at 1 mil; ASTM D-882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | Blown Film at 1 mil; ASTM D-882 | ||
| Coefficient of Friction | 0.15 | 0.15 | Blown Film at 1 mil; ASTM D-1894 | ||
| Elmendorf Tear Strength, MD | 11.8 g/micron | 300 g/mil | Blown Film at 1 mil; ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 25.6 g/micron | 650 g/mil | Blown Film at 1 mil; ASTM D-1922 | ||
| Dart Drop | 4.92 g/micron | 125 g/mil | Blown Film at 1 mil; ASTM D-1709 | ||
| Film Tensile Strength at Break, MD | 55.0 MPa | 7980 psi | Blown Film at 1 mil; ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | Blown Film at 1 mil; ASTM D-882 | ||
| 1% Secant Modulus, MD | 290 MPa | 42000 psi | Blown Film at 1 mil; ASTM D-882 | ||
| 1% Secant Modulus, TD | 345 MPa | 50000 psi | Blown Film at 1 mil; ASTM D-882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 18 % | 18 % | Blown Film at 1 mil; ASTM D-1003 | ||
| Gloss | 65 % | 65 % | 60°, Blown Film at 1 mil; ASTM D-2457 | ||
| Descriptive Properties | |||||
| Process Aid | Yes | ||||