- 熔体流动速率 [g/10min]: 48.0
- 密度 [g/cm3]: 0.939
- 缺口冲击强度: 0.7
- 拉伸强度 [MPa]: 19.0
- 弯曲模量 [MPa]: 640
- 热变形温度 [℃]: 46.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.939 g/cc | 0.0339 lb/in³ | ASTM-D729 |
| Melt Flow | 48 g/10 min @Load 2.16 kg, Temperature 190 °C | 48 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 54 | 54 | ASTM-D2240 |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ASTM-D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM-D638 |
| Elongation at Break | 100 % | 100 % | ASTM-D638 |
| Elongation at Yield | 12 % | 12 % | ASTM-D638 |
| Modulus of Rigidity | 0.645 GPa | 93.6 ksi | ASTM-D747 |
| Flexural Modulus, 1% Secant | 640 MPa | 92800 psi | ASTM-D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM-D256 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ASTM-D648 |
| Vicat Softening Point | 100 °C @Load 1.02 kg | 212 °F @Load 2.25 lb | ASTM-D1525 |