- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D-1505 | ||
| Melt Index of Compound | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D-1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 580 % | 580 % | Cast Film at 1.25 mil; ASTM D-882 | ||
| Film Elongation at Break, TD | 780 % | 780 % | Cast Film at 1.25 mil; ASTM D-882 | ||
| Coefficient of Friction | >= 1.0 | >= 1.0 | Cast Film at 1.25 mil; ASTM D-1894 | ||
| Elmendorf Tear Strength, MD | 11.8 g/micron | 300 g/mil | Cast Film at 1.25 mil; ASTM D-1922 | ||
| Elmendorf Tear Strength, TD | 21.7 g/micron | 550 g/mil | Cast Film at 1.25 mil; ASTM D-1922 | ||
| Dart Drop | 5.51 g/micron | 140 g/mil | Cast Film at 1.25 mil; ASTM D-1709 | ||
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | Cast Film at 1.25 mil; ASTM D-882 | ||
| Film Tensile Strength at Break, TD | 33.0 MPa | 4790 psi | Cast Film at 1.25 mil; ASTM D-882 | ||
| 1% Secant Modulus, MD | 200 MPa | 29000 psi | Cast Film at 1.25 mil; ASTM D-882 | ||
| 1% Secant Modulus, TD | 214 MPa | 31000 psi | Cast Film at 1.25 mil; ASTM D-882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Slip | 0.00 | 0.00 | |||
| Antiblock | 0.00 | 0.00 | |||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | Cast Film at 1.25 mil; ASTM D-1003 | ||
| Gloss | 140 % | 140 % | 60°, Cast Film at 1.25 mil; ASTM D-2457 | ||
| Descriptive Properties | |||||
| Process Aid | None | ||||