- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 | ||
| Thickness | 31.8 microns | 1.25 mil | |||
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | ASTM D1238E | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 560 % | 560 % | ASTM D882 | ||
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 | ||
| Coefficient of Friction | 1.0 | 1.0 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 16.5 g/micron | 420 g/mil | Notched; ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 33.1 g/micron | 840 g/mil | Notched; ASTM D1992 | ||
| Dart Drop | 4.72 g/micron | 120 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 52.4 MPa | 7600 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 42.7 MPa | 6200 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 241 MPa | 35000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 310 MPa | 45000 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 11 % | 11 % | ASTM D1003 | ||
| Gloss | 60 % | 60 % | 45°; ASTM D2457 | ||
| 100 % | 100 % | 60°; ASTM D2457 | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 204 °C | 399 °F | |||
| Die Opening | 0.0762 cm | 0.0300 in | |||
| Extruder Size | 6.35 cm | 2.50 in | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.
Users of our Advanced Search (registration required) may exclude discontinued materials from search results.