- 熔体流动速率 [g/10min]: 0.9
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Melt Flow | 0.90 g/10 min | 0.90 g/10 min | Condition 190/2.16; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.0 MPa | 1450 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | 2 in per min; ASTM D882 |
| Film Elongation at Break, MD | 500 % | 500 % | 2 in per min; ASTM D882 |
| Film Elongation at Break, TD | 600 % | 600 % | 2 in per min; ASTM D882 |
| Coefficient of Friction, Dynamic | 0.70 | 0.70 | ASTM D1894 |
| Coefficient of Friction, Static | 1.0 | 1.0 | ASTM D1894 |
| Elmendorf Tear Strength MD | 210 g | 210 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 420 g | 420 g | ASTM D1922 |
| Dart drop Test | 800 g | 1.76 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 34.0 MPa | 4930 psi | 2 in per min; ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | 2 in per min; ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 5.0 % | 5.0 % | ASTM D1003 |