- 熔体流动速率 [g/10min]: 0.85
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D4883 |
| Melt Flow | 0.85 g/10 min | 0.85 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 610 % | 610 % | ASTM D882 |
| Film Elongation at Break, TD | 770 % | 770 % | ASTM D882 |
| Secant Modulus, MD | 0.150 GPa | 21.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 19.7 g/micron | 500 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 30.7 g/micron | 780 g/mil | ASTM D1922 |
| Dart Drop | 13.5 g/micron | 343 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 430 g | 0.948 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 47.1 MPa | 6830 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.3 MPa | 4970 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 22 % | 22 % | ASTM D2457 |
| Gloss | 40 % | 40 % | 45°. ASTM D 2457 |
| 63 % | 63 % | 60°. ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 227 - 232 °C | 441 - 450 °F | |