- 熔体流动速率 [g/10min]: 0.4
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D4883 |
| Melt Flow | 0.40 g/10 min | 0.40 g/10 min | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 550 % | 550 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.180 GPa | 26.1 ksi | ASTM D882 |
| Secant Modulus, TD | 0.190 GPa | 27.6 ksi | ASTM D882 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 20.9 g/micron | 530 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 31.1 g/micron | 790 g/mil | ASTM D1922 |
| Dart Drop | 40.3 g/micron | 1020 g/mil | F-50 at 26 in.; ASTM D1709 |
| Dart drop Test | 1280 g | 2.82 lb | F-50 at 26 in.; ASTM D1709 |
| Film Tensile Strength at Break, MD | 52.0 MPa | 7540 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 41.2 MPa | 5980 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ASTM D2457 |
| Gloss | 54 % | 54 % | 45°. ASTM D 2457 |
| 87 % | 87 % | 60°, ASTM D 2457 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 232 °C | 450 °F | |