- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.9218
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9218 g/cc | 0.03330 lb/in³ | ASTM D792 |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | ASTM D1238 |
| Antiblock Level | 3000 ppm | 3000 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 10.43 MPa | 1513 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.07 MPa | 1606 psi | ASTM D882 |
| Film Elongation at Break, MD | 463 % | 463 % | ASTM D882 |
| Film Elongation at Break, TD | 657 % | 657 % | ASTM D882 |
| Secant Modulus, MD | 0.178574 GPa | 25.9004 ksi | 2% Secant; ASTM D882 |
| Secant Modulus, TD | 0.200637 GPa | 29.1005 ksi | 2% Secant; ASTM D882 |
| Impact | 112 | 112 | [ft-lbf/in3]; Puncture Resistance; Dow Method |
| 983 | 983 | [ft-lbf/in3]; Toughness MD; ASTM D882 | |
| 1043 | 1043 | [ft-lbf/in3]; Toughness TD; ASTM D882 | |
| Elmendorf Tear Strength MD | 233 g | 233 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 629 g | 629 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.467 g/micron | 291.25 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 30.955 g/micron | 786.25 g/mil | ASTM D1922 |
| Dart drop Test | 159 g | 0.351 lb | Method A; ASTM D1709 |
| Film Tensile Strength at Break, MD | 39.11 MPa | 5673 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 26.36 MPa | 3823 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 122 °C | 252 °F | Dow Method (DSC) |
| Vicat Softening Point | 105 °C | 221 °F | ASTM D1525 |
| Optical Properties | Metric | English | Comments |
| Haze | 11.7 % | 11.7 % | ASTM D1003 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |