- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.919
- 拉伸强度 [MPa]: 11.7
- 弯曲强度 [MPa]: 15.9
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | |
| Thickness | 30.0 microns | 1.18 mil | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg | 6.0 g/10 min @Load 4.76 lb | Melt flow ratio I10/I2 is 7.6. |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 15.9 MPa | 2310 psi | Molded property |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | |
| Film Tensile Strength at Yield, TD | 8.30 MPa | 1200 psi | |
| Tensile Strength, Yield | 11.7 MPa | 1700 psi | Molded property |
| Film Elongation at Break, MD | 660 % | 660 % | |
| Film Elongation at Break, TD | 800 % | 800 % | |
| Elongation at Break | 770 % | 770 % | Molded value |
| Modulus of Elasticity | 0.0110 GPa | 1.60 ksi | Molded sample |
| 0.255 GPa | 37.0 ksi | 2% secant modulus | |
| Elmendorf Tear Strength MD | 300 g | 300 g | |
| Elmendorf Tear Strength TD | 540 g | 540 g | |
| Elmendorf Tear Strength, MD | 10.0 g/micron | 254 g/mil | |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 457 g/mil | |
| Dart Drop | 4.00 g/micron | 102 g/mil | |
| Film Tensile Strength at Break, MD | 46.2 MPa | 6700 psi | |
| Film Tensile Strength at Break, TD | 33.8 MPa | 4900 psi | |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 97.2 °C | 207 °F | |
| Optical Properties | Metric | English | Comments |
| Haze | 1.3 % | 1.3 % | |
| Gloss | 95 % | 95 % | 45° |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 274 °C | 525 °F | Film extrusion temperature |