- 熔体流动速率 [g/10min]: 4.0
- 密度 [g/cm3]: 0.917
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.917 g/cc | 0.0331 lb/in³ | ASTM D4883 | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 4.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.00 MPa | 1020 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 570 % | 570 % | ASTM D882 | ||
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 | ||
| Secant Modulus, MD | 0.152 GPa | 22.0 ksi | 1% Secant; ASTM D882 | ||
| Secant Modulus, TD | 0.158 GPa | 22.9 ksi | 1% Secant; ASTM D882 | ||
| Elmendorf Tear Strength MD | 550 g | 550 g | |||
| Elmendorf Tear Strength TD | 630 g | 630 g | |||
| Elmendorf Tear Strength, MD | 27.0 g/micron | 686 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 31.0 g/micron | 787 g/mil | ASTM D1922 | ||
| Dart Drop | 6.90 g/micron | 175 g/mil | ASTM D1709A | ||
| Film Tensile Strength at Break, MD | 30.0 MPa | 4350 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 20.0 MPa | 2900 psi | ASTM D882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.4 % | 1.4 % | ASTM D1003 | ||
| Gloss | 95 % | 95 % | at 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Process | Film | ||||
| region | US & Canada | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.