- 熔体流动速率 [g/10min]: 35.0
- 密度 [g/cm3]: 0.926
- 拉伸强度 [MPa]: 13.0
- 弯曲模量 [MPa]: 0.480
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | 1.0 hour | 1.0 hour | F50, Condition A, ASTM D1693 |
| Melt Flow | 35 g/10 min @Load 2.16 kg, Temperature 190 °C | 35 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| Elongation at Break | 190 % | 190 % | ASTM D638 |
| Flexural Modulus | 0.480 GPa | 69.6 ksi | ASTM D790 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 160 - 230 °C | 320 - 446 °F | |