- 熔体流动速率 [g/10min]: 105.0
- 密度 [g/cm3]: 0.931
- 拉伸强度 [MPa]: 14.0
- 弯曲模量 [MPa]: 0.520
- 脆化温度 [℃]: -30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.931 g/cc | 0.0336 lb/in³ | ASTM D792 |
| Melt Flow | 105 g/10 min @Load 2.16 kg, Temperature 190 °C | 105 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Spiral Flow | 45.7 cm | 18.0 in | NOVA Snake Flow Test |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 56 | 56 | ASTM D2240 |
| Tensile Strength, Yield | 14.0 MPa | 2030 psi | ASTM D638 |
| Flexural Modulus | 0.520 GPa | 75.4 ksi | ASTM D790 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 100 °C | 212 °F | ASTM D1525 |
| Brittleness Temperature | -30.0 °C | -22.0 °F | ASTM D746 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 170 - 260 °C | 338 - 500 °F | |