- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.926
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | ASTM D792 |
| Thickness | 38.1 microns | 1.50 mil | |
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 14.0 MPa | 2030 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Secant Modulus, MD | 0.210 GPa | 30.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.250 GPa | 36.3 ksi | ASTM D882 |
| Coefficient of Friction | <= 0.20 | <= 0.20 | ASTM D1894 |
| Elmendorf Tear Strength, MD | 6.30 g/micron | 160 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 21.7 g/micron | 551 g/mil | ASTM D1922 |
| Dart Drop | 5.50 g/micron | 140 g/mil | F 50; ASTM D1709/A |
| Film Tensile Strength at Break, MD | 44.0 MPa | 6380 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 18 % @Thickness 0.0250 mm | 18 % @Thickness 0.000984 in | ASTM D1003 |
| Gloss | 37 % | 37 % | 45°; 1 mil; ASTM D1894 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 195 - 220 °C | 383 - 428 °F | |