- 熔体流动速率 [g/10min]: 1.7
- 密度 [g/cm3]: 0.91
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.910 g/cc | 0.0329 lb/in³ | ASTM D1505 |
| Water Vapor Transmission | 5.60 g/m²/day | 0.361 g/100 in²/day | 100% Humidity; ASTM F372 |
| Thickness | 50.8 microns | 2.00 mil | 2:1 BUR |
| Melt Flow | 1.7 g/10 min | 1.7 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.80 MPa | 1280 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.70 MPa | 1410 psi | ASTM D882 |
| Film Elongation at Break, MD | 840 % | 840 % | ASTM D882 |
| Film Elongation at Break, TD | 840 % | 840 % | ASTM D882 |
| Film Elongation at Yield, MD | 30 % | 30 % | ASTM D882 |
| Film Elongation at Yield, TD | 12 % | 12 % | ASTM D882 |
| Elmendorf Tear Strength MD | 270 g | 270 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 590 g | 590 g | ASTM D1922 |
| Film Tensile Strength at Break, MD | 28.7 MPa | 4160 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 22.1 MPa | 3210 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 82.0 °C | 180 °F | ASTM D1525 |