- 熔体流动速率 [g/10min]: 1.4
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.934 g/cc | 0.934 g/cc | ISO 1183 |
| Thickness | 15.0 - 50.0 microns | 0.591 - 1.97 mil | Recommended |
| Melt Flow | 1.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 16.0 MPa | 2320 psi | ISO 527-3 |
| Film Tensile Strength at Yield, TD | 18.0 MPa | 2610 psi | ISO 527-3 |
| Film Elongation at Break, MD | 650 % | 650 % | ISO 527-3 |
| Film Elongation at Break, TD | 800 % | 800 % | ISO 527-3 |
| Coefficient of Friction, Dynamic | >= 0.50 | >= 0.50 | ISO 8295 |
| Elmendorf Tear Strength, MD | 0.7133 g/micron | 18.12 g/mil | ISO 6383-2 |
| Elmendorf Tear Strength, TD | 6.114 g/micron | 155.3 g/mil | ISO 6383-2 |
| Dart drop Test | 55.0 g | 0.121 lb | F50; ISO 7765-1 |
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ISO 527-3 |
| Film Tensile Strength at Break, TD | 32.0 MPa | 4640 psi | ISO 527-3 |
| 1% Secant Modulus, MD | 390 MPa | 56600 psi | ISO 527-3 |
| 1% Secant Modulus, TD | 450 MPa | 65300 psi | ISO 527-3 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Internal method |
| Vicat Softening Point | 117 °C @Load 1.00 kg | 243 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |
| Optical Properties | Metric | English | Comments |
| Haze | 14 % | 14 % | ISO 14782 |
| Gloss | 50 % | 50 % | 45°; ASTM D2457 |