- 熔体流动速率 [g/10min]: 26.0
- 拉伸强度 [MPa]: 9.0
- 弯曲模量 [MPa]: 0.150
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.922 g/cc | 0.922 g/cc | ISO 1183 |
| Melt Flow | 26 g/10 min @Load 2.16 kg, Temperature 190 °C | 26 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 48 | 48 | ISO 868/A |
| Tensile Strength at Break | 10.0 MPa | 1450 psi | ISO 527 |
| Tensile Strength, Yield | 9.00 MPa | 1310 psi | ISO 527 |
| Elongation at Break | >= 500 % | >= 500 % | ISO 527 |
| Flexural Modulus | 0.150 GPa | 21.8 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 117 °C | 243 °F | Internal method |
| Vicat Softening Point | 88.0 °C @Load 1.00 kg | 190 °F @Load 2.20 lb | ISO 306/A |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |