- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D4703 / D1505 | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Antiblock Level | 2500 ppm | 2500 ppm | |||
| Slip Level | 750 ppm | 750 ppm | |||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 | ||
| Film Elongation at Break, TD | 520 % | 520 % | ASTM D882 | ||
| Coefficient of Friction | 0.22 | 0.22 | ASTM D1894 | ||
| Elmendorf Tear Strength, MD | 11.0 g/micron | 279 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 20.0 g/micron | 508 g/mil | ASTM D1922 | ||
| Dart Drop | 30.0 g/micron | 762 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 40.0 MPa | 5800 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 176 MPa | 25500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 176 MPa | 25500 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 118 °C | 244 °F | Peak Melting Temperature; ASTM D3418 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 6.0 % | 6.0 % | ASTM D1003 | ||
| Gloss | 11 % | 11 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | PPA and Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.