- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.58 MPa | 1100 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 | ||
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 | ||
| Puncture Energy | 4.30 J | 3.17 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 9.350 g/micron | 237.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 24.6 g/micron | 625 g/mil | ASTM D1922 | ||
| Dart Drop | 6.89 g/micron | 175 g/mil | ASTM D1709 | ||
| Dart drop Test | 140 g | 0.309 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 73.8 MPa | 10700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 46.7 MPa | 6770 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 110 MPa | 16000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 114 °C | 237 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.4 % | 2.4 % | ASTM D1003 | ||
| Gloss | 86 % | 86 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.