- 熔体流动速率 [g/10min]: 3.5
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Thickness | 20.3 microns | 0.800 mil | |||
| Melt Flow | 3.5 g/10 min | 3.5 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 8.27 MPa | 1200 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 7.58 MPa | 1100 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 510 % | 510 % | ASTM D882 | ||
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 | ||
| Puncture Energy | 4.30 J | 3.17 ft-lb | Exxon Mobil Method | ||
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 | ||
| Elmendorf Tear Strength TD | 500 g | 500 g | ASTM D1922 | ||
| Elmendorf Tear Strength, MD | 9.350 g/micron | 237.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 24.6 g/micron | 625 g/mil | ASTM D1922 | ||
| Dart Drop | 6.89 g/micron | 175 g/mil | ASTM D1709 | ||
| Dart drop Test | 140 g | 0.309 lb | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 73.8 MPa | 10700 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 46.7 MPa | 6770 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 110 MPa | 16000 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 114 °C | 237 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 2.4 % | 2.4 % | ASTM D1003 | ||
| Gloss | 86 % | 86 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||