- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 7.72 MPa | 1120 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.96 MPa | 1010 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 450 % | 450 % | ASTM D882 | ||
| Film Elongation at Break, TD | 850 % | 850 % | ASTM D882 | ||
| Puncture Energy | 2.71 J | 2.00 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 1.48 g/micron | 37.5 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 17.22 g/micron | 437.5 g/mil | ASTM D1922 | ||
| Dart Drop | 3.44 g/micron | 87.5 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 56.5 MPa | 8190 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 28.8 MPa | 4180 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 109 MPa | 15800 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 125 MPa | 18200 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 120 °C | 248 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Crystallization Temperature | 104 °C | 219 °F | ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.6 % | 1.6 % | ASTM D1003 | ||
| Gloss | 92 % | 92 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.