- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ExxonMobil Method | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | ExxonMobil Method | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 | ||
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 | ||
| Elmendorf Tear Strength, MD | 12.0 g/micron | 305 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 16.0 g/micron | 406 g/mil | ASTM D1922 | ||
| Dart Drop | 55.00 g/micron | 1397 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 75.8 MPa | 11000 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 65.5 MPa | 9500 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 169 MPa | 24500 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 179 MPa | 26000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 118 °C | 244 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 3.0 % | 3.0 % | ASTM D1003 | ||
| Gloss | 13 % | 13 % | 60° angle; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | PPA and Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.