- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ExxonMobil Method | ||
| Thickness | 25.4 microns | 1.00 mil | |||
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 10.8 MPa | 1560 psi | at 2% offset; ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 12.1 MPa | 1750 psi | at 2% offset; ASTM D882 | ||
| Film Elongation at Break, MD | 460 % | 460 % | ASTM D882 | ||
| Film Elongation at Break, TD | 760 % | 760 % | ASTM D882 | ||
| Puncture Energy | 3.39 J | 2.50 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 16.1 g/micron | 410 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 30.3 g/micron | 770 g/mil | ASTM D1922 | ||
| Dart Drop | 5.91 g/micron | 150 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 69.50 MPa | 10080 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 55.1 MPa | 7990 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 237 MPa | 34400 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 292 MPa | 42400 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 124 °C | 255 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 12.9 % | 12.9 % | ASTM D1003 | ||
| Gloss | 51 % | 51 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.