- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.918
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.9180 g/cc | 0.03316 lb/in³ | ExxonMobil Method | ||
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 6.89 MPa | 1000 psi | ASTM D882 | ||
| Film Tensile Strength at Yield, TD | 6.76 MPa | 980 psi | ASTM D882 | ||
| Film Elongation at Break, MD | 530 % | 530 % | ASTM D882 | ||
| Film Elongation at Break, TD | 830 % | 830 % | ASTM D882 | ||
| Puncture Energy | 2.94 J | 2.17 ft-lb | ExxonMobil | ||
| Elmendorf Tear Strength, MD | 9.84 g/micron | 250 g/mil | ASTM D1922 | ||
| Elmendorf Tear Strength, TD | 22.4 g/micron | 570 g/mil | ASTM D1922 | ||
| Dart Drop | 3.54 g/micron | 90.0 g/mil | ASTM D1709 | ||
| Film Tensile Strength at Break, MD | 58.6 MPa | 8500 psi | ASTM D882 | ||
| Film Tensile Strength at Break, TD | 36.5 MPa | 5300 psi | ASTM D882 | ||
| 1% Secant Modulus, MD | 11.7 MPa | 1700 psi | ASTM D882 | ||
| 1% Secant Modulus, TD | 124 MPa | 18000 psi | ASTM D882 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 122 °C | 252 °F | Peak Melting Temperature; ExxonMobil Method | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 1.7 % | 1.7 % | ASTM D1003 | ||
| Gloss | 90 % | 90 % | 45°; ASTM D2457 | ||
| Descriptive Properties | |||||
| Features | Thermal Stabilizer | ||||