- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
- 透光率 [%]: 90.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 1.0 g/10 min | 1.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D882 |
| Film Elongation at Break, MD | 600 % | 600 % | ASTM D882 |
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D882 |
| Secant Modulus, MD | 0.183 GPa | 26.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.217 GPa | 31.5 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 120 g | 120 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 550 g | 550 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 3.94 g/micron | 100 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 18.0 g/micron | 458 g/mil | ASTM D1922 |
| Dart Drop | 2.80 g/micron | 71.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 85.0 g | 0.187 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 43.0 MPa | 6240 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 60 % | 60 % | 45°, ASTM D-2457 |
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |