- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.925
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.925 g/cc | 0.0334 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 1.5 g/10 min | 1.5 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 13.0 MPa | 1890 psi | ASTM D882 |
| Film Elongation at Break, MD | 670 % | 670 % | ASTM D882 |
| Film Elongation at Break, TD | 790 % | 790 % | ASTM D882 |
| Secant Modulus, MD | 0.296 GPa | 42.9 ksi | ASTM D882 |
| Secant Modulus, TD | 0.324 GPa | 47.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 80 g | 80 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 2.64 g/micron | 67.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 9.84 g/micron | 250 g/mil | ASTM D1922 |
| Dart Drop | 2.28 g/micron | 58.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 70.0 g | 0.154 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 46.0 MPa | 6670 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 37.0 MPa | 5370 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 123 °C | 253 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 16 % | 16 % | ASTM D1003 |
| Gloss | 46 % | 46 % | 45°, ASTM D-2457 |