- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 10.0
- 弯曲强度 [MPa]: 21.0
- 弯曲模量 [MPa]: 0.218
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | Exxon Method |
| Environmental Stress Crack Resistance | >= 1000 hour | >= 1000 hour | F50, Igepal, Condition C; ASTM D1693 |
| Melt Flow | 2.0 g/10 min | 2.0 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 45 | 45 | ASTM D2240 |
| Tensile Strength, Ultimate | 21.0 MPa | 3050 psi | ASTM D638 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | ASTM D638 |
| Elongation at Break | 800 % | 800 % | |
| Flexural Modulus | 0.218 GPa | 31.6 ksi | ASTM D790 |
| Tensile Impact Strength | 231 kJ/m² | 110 ft-lb/in² | 23°C; ASTM D-1822 |
| Dart Drop, Total Energy | 37.0 J | 27.3 ft-lb | Temp @ -40°C; F50; ASTM D-3029 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 121 °C | 250 °F | Exxon Method |
| Brittleness Temperature | -70.0 °C | -94.0 °F | ASTM D746 |