- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 30.5 microns | 1.20 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.0 MPa | 1600 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Elongation at Break, MD | 590 % | 590 % | ASTM D882 |
| Film Elongation at Break, TD | 730 % | 730 % | ASTM D882 |
| Secant Modulus, MD | 0.272 GPa | 39.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.317 GPa | 46.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 340 g | 340 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 760 g | 760 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 11.1 g/micron | 283 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.9 g/micron | 633 g/mil | ASTM D1922 |
| Dart Drop | 8.54 g/micron | 217 g/mil | F50; ASTM D1709 |
| Dart drop Test | 260 g | 0.573 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 63.9 MPa | 9270 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 55.4 MPa | 8040 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 10 % | 10 % | ASTM D1003 |
| Gloss | 54 % | 54 % | 45°, ASTM D-2457 |