- 熔体流动速率 [g/10min]: 3.2
- 密度 [g/cm3]: 0.9175
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.9175 g/cc | 0.03315 lb/in³ | Exxon Method |
| Thickness | 20.3 microns | 0.800 mil | |
| Melt Flow | 3.2 g/10 min | 3.2 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 8.00 MPa | 1160 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 8.00 MPa | 1160 psi | ASTM D882 |
| Film Elongation at Break, MD | 430 % | 430 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Secant Modulus, MD | 0.131 GPa | 19.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.159 GPa | 23.1 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 180 g | 180 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 770 g | 770 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 8.86 g/micron | 225 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 37.9 g/micron | 963 g/mil | ASTM D1922 |
| Dart Drop | 3.70 g/micron | 94.0 g/mil | F50; ASTM D1709 |
| Dart drop Test | 75.0 g | 0.165 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 61.0 MPa | 8850 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.0 MPa | 4930 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 124 °C | 255 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 1.0 % | 1.0 % | ASTM D1003 |
| Gloss | 96 % | 96 % | 45°, ASTM D-2457 |