- 熔体流动速率 [g/10min]: 0.5
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 15.2 microns | 0.600 mil | |
| Melt Flow | 0.50 g/10 min | 0.50 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 12.0 MPa | 1740 psi | ASTM D882 |
| Film Elongation at Break, MD | 420 % | 420 % | ASTM D882 |
| Film Elongation at Break, TD | 680 % | 680 % | ASTM D882 |
| Secant Modulus, MD | 0.241 GPa | 35.0 ksi | ASTM D882 |
| Secant Modulus, TD | 0.269 GPa | 39.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 100 g | 100 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 520 g | 520 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 6.57 g/micron | 167 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 34.1 g/micron | 867 g/mil | ASTM D1922 |
| Dart Drop | 8.54 g/micron | 217 g/mil | F50; ASTM D1709 |
| Dart drop Test | 130 g | 0.287 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 74.5 MPa | 10800 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 52.0 MPa | 7540 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 125 °C | 257 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 8.5 % | 8.5 % | ASTM D1003 |
| Gloss | 58 % | 58 % | 45°, ASTM D-2457 |