- 熔体流动速率 [g/10min]: 1.3
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | Exxon Method |
| Thickness | 17.8 microns | 0.700 mil | |
| Melt Flow | 1.3 g/10 min | 1.3 g/10 min | Exxon Method |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 11.4 MPa | 1650 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 11.9 MPa | 1730 psi | ASTM D882 |
| Film Elongation at Break, MD | 480 % | 480 % | ASTM D882 |
| Film Elongation at Break, TD | 690 % | 690 % | ASTM D882 |
| Secant Modulus, MD | 0.226 GPa | 32.8 ksi | ASTM D882 |
| Secant Modulus, TD | 0.276 GPa | 40.0 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 190 g | 190 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 720 g | 720 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 10.7 g/micron | 271 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 40.51 g/micron | 1029 g/mil | ASTM D1922 |
| Dart Drop | 5.63 g/micron | 143 g/mil | F50; ASTM D1709 |
| Dart drop Test | 100 g | 0.221 lb | F50; ASTM D-1709 |
| Film Tensile Strength at Break, MD | 57.6 MPa | 8350 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 38.6 MPa | 5600 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 126 °C | 259 °F | Exxon Method |
| Optical Properties | Metric | English | Comments |
| Haze | 30.4 % | 30.4 % | ASTM D1003 |
| Gloss | 24 % | 24 % | 45°, ASTM D-2457 |