- 熔体流动速率 [g/10min]: 2.0
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 20.0 microns | 0.787 mil | |
| Melt Flow | 2.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.0 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 500 % | 500 % | ASTM D882 |
| Film Elongation at Break, TD | 915 % | 915 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 11.6 g/micron | 295 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 24.7 g/micron | 628 g/mil | ASTM D1922 |
| Dart Drop | 3.66 g/micron | 93.0 g/mil | ASTM D1709 |
| Film Tensile Strength at Break, MD | 44.82 MPa | 6500 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 34.47 MPa | 5000 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 1.7 % | 1.7 % | ASTM D1003 |
| Gloss | 98 % | 98 % | 45°; ASTM D2457 |