- 熔体流动速率 [g/10min]: 0.95
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 g/cc | 0.0332 lb/in³ | ASTM D1505 |
| Thickness | 25.0 microns | 0.984 mil | |
| Melt Flow | 0.95 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.95 g/10 min @Load 4.76 lb, Temperature 374 °F | Condition E; ASTM D1238 |
| Antiblock Level | 1700 ppm | 1700 ppm | |
| Slip Level | 1350 ppm | 1350 ppm | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 690 % | 690 % | ASTM D882 |
| Film Elongation at Break, TD | 920 % | 920 % | ASTM D882 |
| Elmendorf Tear Strength MD | 150 g | 150 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 385 g | 385 g | ASTM D1922 |
| Dart drop Test | 135 g | 0.298 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.2 MPa | 5100 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 28.5 MPa | 4130 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 20 % | 20 % | ASTM D1003 |
| Gloss | 40 % | 40 % | 45°C; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Blow-up Ratio (BUR) | 2.5 | 2.5 | |