- 熔体流动速率 [g/10min]: 0.65
- 密度 [g/cm3]: 0.919
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.919 - 0.921 g/cc | 0.0332 - 0.0333 lb/in³ | ASTM D1505 |
| Melt Flow | 0.65 - 0.85 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.65 - 0.85 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D882 |
| Film Tensile Strength at Yield, TD | 9.50 MPa | 1380 psi | ASTM D882 |
| Film Elongation at Break, MD | 700 % | 700 % | ASTM D882 |
| Film Elongation at Break, TD | 800 % | 800 % | ASTM D882 |
| Elmendorf Tear Strength, MD | 5.12 g/micron | 130 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 13.8 g/micron | 350 g/mil | ASTM D1922 |
| Dart drop Test | 80.0 g | 0.176 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 35.0 MPa | 5080 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 30.0 MPa | 4350 psi | ASTM D882 |