- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.936
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.936 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| Thickness | 25.4 microns | 1.00 mil | |
| Melt Flow | 2.2 g/10 min | 2.2 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 470 % | 470 % | ASTM D882 |
| Film Elongation at Break, TD | >= 700 % | >= 700 % | ASTM D882 |
| Secant Modulus, MD | 0.300 GPa | 43.5 ksi | ASTM D882 |
| Secant Modulus, TD | 0.340 GPa | 49.3 ksi | ASTM D882 |
| Elmendorf Tear Strength MD | 43 g | 43 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 760 g | 760 g | ASTM D1922 |
| Elmendorf Tear Strength, MD | 1.69 g/micron | 43.0 g/mil | ASTM D1922 |
| Elmendorf Tear Strength, TD | 29.9 g/micron | 760 g/mil | ASTM D1922 |
| Dart Drop | 2.52 g/micron | 64.0 g/mil | ASTM D1709 |
| Dart drop Test | 64.0 g | 0.141 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 19.0 MPa | 2760 psi | ASTM D882 |
| Optical Properties | Metric | English | Comments |
| Haze | 2.6 % | 2.6 % | ASTM D1003 |
| Gloss | 91 % | 91 % | at 45°; ASTM D523 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 260 - 290 °C | 500 - 554 °F | |