- 熔体流动速率 [g/10min]: 2.2
- 密度 [g/cm3]: 0.92
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.920 g/cc | 0.0332 lb/in³ | ISO 1183 |
| Melt Flow | 2.2 g/10 min @Load 2.16 kg, Temperature 190 °C | 2.2 g/10 min @Load 4.76 lb, Temperature 374 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Stress | 10.0 MPa | 1450 psi | MD; ISO 527 |
| 11.0 MPa | 1600 psi | TD; ISO 527 | |
| Film Elongation at Break, MD | 600 % | 600 % | ISO 527 |
| Film Elongation at Break, TD | 800 % | 800 % | ISO 527 |
| Elmendorf Tear Strength MD | 110 g | 110 g | ASTM D1922 |
| Elmendorf Tear Strength TD | 300 g | 300 g | ASTM D1922 |
| Dart drop Test | 130 g | 0.287 lb | ASTM D1709 |
| Film Tensile Strength at Break, MD | 36.0 MPa | 5220 psi | ISO 527 |
| Film Tensile Strength at Break, TD | 28.0 MPa | 4060 psi | ISO 527 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 93.0 °C | 199 °F | ISO 306 |
| Processing Properties | Metric | English | Comments |
| Mold Temperature | 225 °C | 437 °F | |