- 熔体流动速率 [g/10min]: 1.5
- 密度 [g/cm3]: 0.918
- 拉伸强度 [MPa]: 9.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.918 - 0.923 g/cc @Temperature 23.0 °C | 0.0332 - 0.0333 lb/in³ @Temperature 73.4 °F | |||
| 0.920 - 0.925 g/cc @Temperature 20.0 °C | 0.0332 - 0.0334 lb/in³ @Temperature 68.0 °F | ||||
| Melt Flow | 1.5 - 2.4 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.5 - 2.4 g/10 min @Load 4.76 lb, Temperature 374 °F | ±10% | ||
| 30 - 84 g/10 min @Load 21.6 kg, Temperature 190 °C | 30 - 84 g/10 min @Load 47.6 lb, Temperature 374 °F | ||||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | >= 9.00 MPa | >= 1310 psi | |||
| Elongation at Break | >= 700 % | >= 700 % | |||
| Tear Strength Test | >= 20 | >= 20 | MPa | ||
| Descriptive Properties | |||||
| Amount of impurities [pcs] | 8 | ||||