- 熔体流动速率 [g/10min]: 6.0
- 密度 [g/cm3]: 0.935
- 拉伸强度 [MPa]: 16.0
- 弯曲模量 [MPa]: 0.650
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.935 g/cc | 0.0338 lb/in³ | ASTM D1505 |
| Melt Flow | 6.0 - 9.0 g/10 min | 6.0 - 9.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 52 | 52 | ASTM D1706 |
| Tensile Strength, Yield | 16.0 - 17.0 MPa | 2320 - 2470 psi | 50mm/min; ASTM D638-64T |
| Elongation at Break | 400 - 500 % | 400 - 500 % | ASTM D638-64T |
| Flexural Modulus | 0.650 GPa | 94.3 ksi | ASTM D760-66 |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 115 °C | 239 °F | ASTM D1525 |
| Brittleness Temperature | -70.0 °C | -94.0 °F | ASTM D746 |