- 熔体流动速率 [g/10min]: 30.0
- 密度 [g/cm3]: 0.87
- 弯曲模量 [MPa]: 0.0172
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.870 g/cc | 0.0314 lb/in³ | ASTM D1505 | ||
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Shore A | 72 | 72 | ASTM D2240 | ||
| Film Tensile Strength at Yield, MD | 1.34 MPa | 195 psi | ASTM D882 | ||
| Film Elongation at Break, MD | >= 1000 % | >= 1000 % | ASTM D882 | ||
| Flexural Modulus | 0.0172 GPa | 2.50 ksi | 2% Secant, in accordance with ASTM D638; ASTM D790 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 75.0 °C | 167 °F | |||
| Vicat Softening Point | 41.1 °C | 106 °F | ASTM D1525 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 165 - 235 °C | 329 - 455 °F | |||
| Mold Temperature | 50.0 - 60.0 °C | 122 - 140 °F | |||
| Injection Pressure | 10.0 - 14.0 MPa | 1450 - 2030 psi | |||
| Descriptive Properties | |||||
| Form | Pellets | ||||
| Injection Rate | Fast | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.