- 熔体流动速率 [g/10min]: 0.8
- 密度 [g/cm3]: 0.921
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 0.921 g/cc | 0.0333 lb/in³ | ASTM D 792 | ||
| Thickness | 25.0 microns | 0.984 mil | As tested for properties on this data sheet | ||
| 25.0 - 150 microns | 0.984 - 5.91 mil | Recommended range for processing | |||
| Melt Flow | 0.80 g/10 min @Load 2.16 kg, Temperature 190 °C | 0.80 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D 1238 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Film Tensile Strength at Yield, MD | 9.00 MPa | 1310 psi | ASTM D 882 | ||
| Film Tensile Strength at Yield, TD | 10.0 MPa | 1450 psi | ASTM D 882 | ||
| Film Elongation at Break, MD | 520 % | 520 % | ASTM D 882 | ||
| Film Elongation at Break, TD | 700 % | 700 % | ASTM D 882 | ||
| Elmendorf Tear Strength MD | 290 g | 290 g | ASTM D 1922 | ||
| Elmendorf Tear Strength TD | 490 g | 490 g | ASTM D 1922 | ||
| Elmendorf Tear Strength, MD | 11.6 g/micron | 295 g/mil | ASTM D 1922 | ||
| Elmendorf Tear Strength, TD | 19.6 g/micron | 498 g/mil | ASTM D 1922 | ||
| Dart Drop | 20.5 g/micron | 521 g/mil | ASTM D 1709/A | ||
| Dart drop Test | 512 g | 1.13 lb | F50; ASTM D 1709/A | ||
| Film Tensile Strength at Break, MD | 50.0 MPa | 7250 psi | ASTM D 882 | ||
| Film Tensile Strength at Break, TD | 42.0 MPa | 6090 psi | ASTM D 882 | ||
| 1% Secant Modulus, MD | 174 MPa | 25200 psi | ASTM D 882 | ||
| 1% Secant Modulus, TD | 188 MPa | 27300 psi | ASTM D 882 | ||
| Optical Properties | Metric | English | Comments | ||
| Haze | 21 % | 21 % | ASTM D 1003 | ||
| Gloss | 33 % | 33 % | At 45°; ASTM D 2457 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Recommended | ||
| Die Opening | 0.0889 - 0.203 cm | 0.0350 - 0.0800 in | Recommended range | ||
| Descriptive Properties | |||||
| Low Friction Puncture | 53 (J/mm) | NOVA Chemicals test method | |||