- 熔体流动速率 [g/10min]: 1.0
- 密度 [g/cm3]: 0.918
- 缺口冲击强度: 6.8
- 拉伸强度 [MPa]: 10.0
- 弯曲模量 [MPa]: 0.400
- 脆化温度 [℃]: -70.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.918 g/cc | 0.0332 lb/in³ | ASTM D792 |
| Environmental Stress Crack Resistance | >= 2500 hour | >= 2500 hour | F0; Condition C, 100% Igepal; ASTM D1693 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 190 °C | 1.0 g/10 min @Load 4.76 lb, Temperature 374 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 58 | 58 | ASTM D2240 |
| Tensile Strength, Yield | 10.0 MPa | 1450 psi | Extension rate 2 in/min; ASTM D638 |
| Elongation at Break | 900 % | 900 % | Extension rate 2 in/min; ASTM D638 |
| Flexural Modulus | 0.400 GPa | 58.0 ksi | 2% Strain; ASTM D3350 |
| Izod Impact, Notched | 6.80 J/cm | 12.7 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | ASTM D696 |
| Maximum Service Temperature, Air | >= 220 °C | >= 428 °F | ASTM D3350 |
| Vicat Softening Point | 104 °C | 219 °F | ASTM D1525 |
| Brittleness Temperature | <= -70.0 °C | <= -94.0 °F | ASTM D746 |